Investigation of corrosion properties with Ni–P/TiNO coating on aluminum alloy bipolar plates in proton exchange membrane fuel cell

Aluminum alloy bipolar plates have unique application potential in proton exchange membrane fuel cell (PEMFC) due to the characteristics of lightweight and low cost. However, extreme susceptibility to corrosion in PEMFC operation condition limits the application. To promote the corrosion resistance of aluminum alloy bipolar plates, a Ni–P/TiNO coating was prepared by electroless plating and closed field unbalanced magnetron sputter ion plating (CFUMSIP) technology on the 6061 Al substrate. The research results show that Ni–P interlayer improves the deposition effect of TiNO outer layer and increase the content of TiN and TiO_xN_y phases. Compared to Ni–P and TiNO single-layer coatings, the Ni–P/TiNO coating samples exhibited the lowest current density value of (1.10 ± 0.02) × 10^?6 A·cm^?2 in simulated PEMFC cathode environment. Additionally, potential cyclic polarization measurements were carried out aiming to evaluate the durability of the aluminum alloy bipolar plate during the PEMFC start-up/shut-up process. The results illustrate that the Ni–P/TiNO coating samples exhibit excellent stability and corrosion resistance.     

Influence of CO2 inleakage on the slight-alkalization of generator internal cooling water

The slight-alkalization of generator internal cooling water (GICW) is widely used to inhibit the corrosion of hollow copper conductor and thereby ensure the safe operation of the generator. CO₂ inleakage is increasingly identified as a potential security risk for GICW system. In this paper, the influence of CO₂ inleakage on the slight-alkalization of GICW was theoretically discussed. Based on the equilibriums of the CO₂-NaOH-H₂O system, CO₂ inleakage saturation was derived to quantify the amount of the dissolved CO₂ in GICW. This parameter can be directly calculated with the measured conductivity and the [Na⁺] of GICW. The influence of CO₂ inleakage on the slight-alkalization conditioning of GICW and the measurement of its water quality parameters were then analyzed. The more severe the inleakage, the narrower the water quality operation ranges of GICW, resulting in the more difficult the slight-alkalization conditioning of GICW. The temperature calibrations of the conductivity and the pH value of GICW show non-linear correlations with the amount of CO₂ inleakage and the NaOH dosage. This study provides insights into the influence of CO₂ inleakage on the slight-alkalization of GICW, which can serve as the theoretical basis for the actual slight-alkalization when CO₂ inleakage occurs.     

机械合金化FeS/Cu复合材料的摩擦磨损性能

以FeS和CuSn8Ni1粉末为原料，利用机械合金化技术和粉末冶金技术制备了FeS/Cu复合材料，探讨了不同载荷情况下所制备的FeS/Cu复合材料的摩擦学性能及润滑膜与转移膜特征。结果表明：机械合金化提高了FeS与铜合金基体界面结合性能，进而提高了材料减摩耐磨性能；当载荷较小时，摩擦副表面接触不稳定，复合转移膜不连续，摩擦因数波动大；载荷较大时，复合转移膜易破损，材料的减摩耐磨性能变差；当载荷为150 N时，载荷适宜，材料表面软化，复合转移膜更加完整，摩擦因数较小。     

热处理对挤压态Mg-6Gd-5Y-1Zn合金组织与性能的影响

通过对Mg-6Gd-5Y-1Zn(质量分数,%)合金在固溶和时效处理状态下显微组织和力学性能的研究发现,α-Mg基体、沿挤压方向分布的条状18R-LPSO相、少量的Mg₂₄(GdYZn)₅ 相以及细层片状的14H-LPSO相构成了挤压态合金的组成相。挤压态合金经固溶(T4)处理后,一部分18R-LPSO相溶入基体,并且基体中的14H-LPSO相伸长同时粗化。挤压态合金经过固溶加时效(T6)处理后,大量β′相从α-Mg基体中析出。T6态合金的室温力学性能最好,其屈服强度、抗拉强度及伸长率分别为272 MPa、406 MPa和6.1%。β′相沉淀也发生在挤压态合金的直接人工时效(T5)处理过程,但相比于T6处理,14H-LPSO相和β′相在基体中的体积分数均偏低。     

变形铝合金表面锆基化学转化膜的研究现状

化学转化膜是金属表面主要的处理方法之一，具备良好的附着力和耐蚀性，能为铝合金提供一定的临时防护。传统的六价铬酸盐化学转化膜在日渐严苛的环保压力下已经逐渐淘汰，取而代之的是近几年发展迅猛的三价铬及无铬锆基化学转化膜。铝合金可分为铸造铝合金和变形铝合金，按照所含主要合金元素和热处理状态可分为若干个系列和型号。本文选取几种典型的变形铝合金，综述了不同铝合金微观组织对转化膜成膜过程的影响，化学转化液添加剂、预处理和后处理工艺对转化膜性能的调控及作用机理，以及几种典型商业钝化剂在变形铝合金表面的应用。总结了目前变形铝合金表面锆基化学转化膜仍面临的问题和发展趋势，未来化学转化膜需在满足新型铝合金发展要求的基础上，通过不同有机、无机添加剂以及外场作用对转化膜的成膜均一性、完整性进行调控，以提高转化膜的综合性能。     

铜电解精炼添加剂生产实践与精细化管理探索

添加剂是铜电解精炼生产管理的最关键要素,合适的添加剂使用方案可以有效保障电解生产系统长期稳定。结合添加剂生产实践和其它电解厂添加剂管理优点,提出探索添加剂精细化管理,进一步保障和提升铜电解添加剂管理实效。     

浅谈不同给液方式在铜电解车间的应用

不同给液方式对铜电解过程中有重要的影响,不同的循环方式会影响槽内温度分布、电解液成分及阳极泥沉降等,因此,根据铜电解生产不同情况的需要,分析对比了多种给液方式在贵冶电解车间的应用,总结了这几种给液方式的优缺点和适用条件。     

脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。     

浅谈压延铜箔光面色差的成因

针对压延铜箔在表面处理过程中光面易出现色差的问题,从设备、工艺、人员操作等方面进行成因探讨,并给出了应对措施。